Thermal strength of the alkali-activated slag concrete | ||
| AUT Journal of Civil Engineering | ||
| مقاله 4، دوره 4، شماره 3، آذر 2020، صفحه 303-314 اصل مقاله (1.71 M) | ||
| نوع مقاله: Research Article | ||
| شناسه دیجیتال (DOI): 10.22060/ajce.2019.16793.5601 | ||
| نویسندگان | ||
| Mohammad Shahbaz* 1؛ kiachehr behfarnia2 | ||
| 1Department of Civil Engineering, University of Isfahan, Isfahan 81746-73441, Iran | ||
| 2Civil Engineering Department, Isfahan University of Technology | ||
| چکیده | ||
| Every structure may experience elevated temperatures during its service life. Heat changes the physical and mechanical properties of concrete. The increasing need for cement for concrete preparation has had an environmental impact including about 7% share of CO2 emissions to the atmosphere. Thus, it is essential to provide alternative products to move on the path of sustainable development to reduce these effects. One of the strategies for environmentally friendly concrete production is to use alkali-activated slag concrete (AASC). Alkali-activated slag (AAS), if designed properly, could be considered as a proper replacement for Portland cement. In this study, alkali-activated slag concrete specimens with different slag contents were placed in a furnace at different temperatures up to 800˚C. The effect of temperature on the mass loss and the compressive strength of the AAS concrete was investigated. Portland cement specimens were also prepared to be compared with the AAS concrete ones. The data was analyzed using the T-test method, as well as one-way and two-way ANOVA. Finally, scanning electron microscopy images were used to compare the microstructures of the concrete at different temperatures and the pore structure of AAS concrete was investigated using mercury intrusion porosimetry. Overall, the results showed the very good thermal performance of the AAS concrete in comparison with that of the Portland cement one. | ||
| کلیدواژه‌ها | ||
| Alkali-activated concrete؛ Slag؛ Mass loss؛ Compressive strength؛ Thermal performance؛ Statistic analysis؛ SEM؛ MIP | ||
| مراجع | ||
|
[1] Y. Ding, J.G. Dai, C.J. Shi, Mechanical properties of alkali-activated concrete: A state-of-the-art review, Construction and Building Materials. 127 (2016) 68-79. [2] J.L. Provis, Geopolymers and other alkali activated materials: why, how, and what?, Materials and Structures. 47 (2014) 11-25. [3] J. Davidovits, Geopolymer chemistry and applications, Geopolymer Institute 2015. [4] C. Shi, D. Roy, P. Krivenko, Alkali-activated cements and concretes, CRC press 2006. [5] K. Behfarnia, M. Hasanzade, Advanced topics in cement and pozzolan: technology, Jahād-e Dāneshgāhi of isfahan. (2014). [6] M. Rostami, K. Behfarnia, The effect of silica fume on durability of alkali activated slag concrete, Construction and Building Materials. 134 (2017) 262–268. [7] J.L. Provis, S.A. Bernal, Geopolymers and related alkali-activated materials, Annual Review of Materials Research. 44 (2014) 299-327. [8] Z. Pan, J.G. Sanjayan, Stress¨Cstrain behaviour and abrupt loss of stiffness of geopolymer at elevated temperatures, Cement and Concrete Composites. 32(9) (2010) 657-664. [9] Z. Pan, J.G. Sanjayan, F. Collins, Effect of transient creep on compressive strength of geopolymer concrete for elevated temperature exposure, Cement and Concrete Research. 56 (2014) 182-189. [10] Z. Pan, J.G. Sanjayan, B.V. Rangan, An investigation of the mechanisms for strength gain or loss of geopolymer mortar after exposure to elevated temperature, Journal of Materials Science. 44(7) (2009) 1873-1880. [11] M. Guerrieri, J. Sanjayan, F. Collins, Residual compressive behavior of alkali-activated concrete exposed to elevated temperatures, Fire and Materials. 33(1) (2009) 51-62. [12] R. Zhao, J.G. Sanjayan, Geopolymer and Portland cement concretes in simulated fire, Magazine of Concrete research. 63(3) (2011) 163-173. [13] D.L. Kong, J.G. Sanjayan, Damage behavior of geopolymer composites exposed to elevated temperatures, Cement and Concrete Composites. 30(10) (2008) 986-991. [14] D.L. Kong, J.G. Sanjayan, Effect of elevated temperatures on geopolymer paste, mortar and concrete, Cement and Concrete Research. 40(2) (2010) 334-339. [15] D.L. Kong, J.G. Sanjayan, K. Sagoe-Crentsil, Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures, Cement and Concrete Research. 37(12) (2007) 1583-1589. [16] İ. Türkmen, M.B. Karakoç, F. Kantarcı, M. M. Maraş, R. Demirboğa, Fire resistance of geopolymer concrete produced from Elazığ ferrochrome slag, Fire and Materials. 40(6) (2016) 836-847. [17] T. Bakharev, Thermal behaviour of geopolymers prepared using class F fly ash and elevated temperature curing, Cement and Concrete Research. 36 (2006) 1134-1147. [18] T.W. Cheng, J.P. Chiu, Fire-resistant geopolymer produced by granulated blast furnace slag, Minerals Engineering. 16 (2003) 205–210. [19] I. Giannopoulou, D. Panias, Fire Resistant geopolymers synthesized from industrial wastes, World Journal of Engineering. 5 (2008) 130-131. [20] Z. Pan, Z. Tao, Y.F. Cao, R. Wuhrer, T. Murphy, Compressive strength and microstructure of alkali activated fly ash/slag binders at high temperature, Cement and Concrete Composites. 86 (2018) 9-18. [21] F. Aslani, Z. Asif, Properties of Ambient-Cured Normal and Heavyweight Geopolymer Concrete Exposed to High Temperatures, Materials, 12(5) (2019) 740. [22] K. Behfarnia, M. Shahbaz, The effect of elevated temperature on the residual tensile strength and physical properties of the alkali[1]activated slag concrete, Journal of Building Engineering. 20 (2018) 442–454. [23] Y.L. Li, X.L. Zhao, R.K. Singh Raman, S. Al-saadi, Thermal and mechanical properties of alkali-activated slag paste, mortar and concrete utilising seawater and sea sand, Construction and Building Materials. 159 (2018) 704-724. [24] The American Society for Testing and Materials, Standard specification for ground granulated blast furnace slag for use in concrete and mortars, ASTM C989. Vol.04.02 (2013). [25] B. Talling, J. Brandstetr, Present state and future of alkali-activated slag concretes, ACI Special Publication. 114 (1989). [26] J. Chang, A study on the setting characteristics of sodium silicate[1]activated slag pastes, Cement and Concrete Research. 33 (2003) 1005- 1011. [27] D. Hardjito, S.E. Wallah, D.M.J. Sumajouw, B.V. Rangan, On the development of fly ash-based geopolymer concrete, ACI Materials Journal. 101(6) (2004) 467-472. [28] S. Aydin, B. Baradan, Mechanical and microstructural properties of heat cured alkali-activated slag mortars, Materials and Design. 35 (2012) 374–383. [29] S.D. Wang, K.L. Scrivener, P.L. Pratt, Factors affecting the strength of alkali activated slag, Cement and Concrete Research. 24(6) (1994) 1033- 1043. [30] M. Shojaei, K. Behfarnia, R. Mohebi, Application of alkali-activated slag concrete in railway sleepers, Materials and Design. 69 (2015) 89–95. [31] The American Society for Testing and Materials, Standard specification for concrete aggregates, ASTM C33. Vol.04.02 (2003). [32] The American Society for Testing and Materials, Standard specification for chemical admixtures for concrete, ASTM C494. Vol.04.02 (2003). [33] BS 1881: part 5, Testing concrete: Methods of testing hardened concrete for other than strength, British Standard Institution. London. (1970). [34] EN 1992-1-2.Eurocode 2: Design of concrete structures- Part 1-2: General rules- Structural fire design, 97 (2004). [35] M. Talha Junaid, A. Khennane, O. Kayali, A. Sadaoui, D. Picard, M. Fafard, Aspects of the deformational behaviour of alkali activated fly ash concrete at elevated temperatures, Cement and Concrete Research. 60 (2014) 24-29. [36] W. Khaliq, H. Anis Khan, High temperature material properties of calcium aluminate cement concrete, Construction and Building Materials. 94 (2015) 475-487. [37] B. Georgali, P.E. Tsakiridis, Microstructure of fire-damaged concrete, Cement and Concrete Composites. 27 (2005) 255-259. [38] K. Sakr, E. El-Hakim, Effect of high temperature or fire on heavy weight concrete properties, Cement and Concrete Research. 35 (2005) 590-596. | ||
|