Experimental evaluation of the effect of Nano-Graphene on the durability of roller-compacted concrete pavements under freeze-thaw cycles | ||
| AUT Journal of Civil Engineering | ||
| دوره 8، شماره 1، 2024، صفحه 43-50 اصل مقاله (566.63 K) | ||
| نوع مقاله: Research Article | ||
| شناسه دیجیتال (DOI): 10.22060/ajce.2024.23224.5865 | ||
| نویسندگان | ||
| SeyedehNajmeh Rezaei Tochaei؛ ata Jafary Shalkoohy* | ||
| Department of Civil Engineering, BandarAnzali Branch, Islamic Azad University, Bandaranzali, Iran | ||
| چکیده | ||
| Millions of dollars are spent every year on road pavements, which generally require rehabilitation every one to five years. Roller-compacted concrete (RCC) pavements are a good replacement for asphalt pavements due to their special properties, such as better durability and conformity with sustainable development principles. On the other hand, changes in the ambient temperature, which cause freeze-thaw cycles, can strongly affect the strength and durability of concrete pavements. Hence, a study of the impact of freeze-thaw cycles and additives on the properties of RCC seems necessary for developing suitable measures for controlling damage and durability loss in concrete. To this end, the present study investigated the influence of cement and nanographene content on the durability of pavements and the weight loss, dynamic modulus of elasticity, durability factor, and spalling of RCC. Nanographene with 0.05%, 0.07%, and 0.1% of cement weight was added to specimens prepared with cement grades of 200, 250, and 300. The specimens were subjected to freeze-thaw cycles after preparation and curing. According to the results, the addition of nanographene improved the properties of RCC under freeze-thaw cycles, reduced weight loss and spalling in the specimens with different cement contents, and enhanced their durability factor and modulus of elasticity. Although adding nanographene significantly contributed to better concrete properties, its effect was directly related to the concrete content. Finally, the optimal values of the cement and graphene content after 300 cycles were obtained to be 300 and 0.05% of cement weight, respectively. | ||
| کلیدواژه‌ها | ||
| RCC؛ Nanographene؛ Strength؛ Durability؛ Freeze-Thaw Cycle | ||
| مراجع | ||
|
[1] A.E. Richardson, K.A. Coventry, S. Wilkinson, Freeze/thaw durability of concrete with synthetic fiber additions, Cold Regions Science and Technology, 83–84 (2012) 49-56.
[2] A. Mardani-Aghabaglou, Ö. Andiç-Çakir, K. Ramyar, Freeze–thaw resistance and transport properties of high-volume fly ash roller compacted concrete designed by maximum density method, Cement and Concrete Composites, 37 (2013) 259-266.
[3] H. Rooholamini, A. Hassani, M.R.M. Aliha, Evaluating the effect of macro-synthetic fibre on the mechanical properties of roller-compacted concrete pavement using response surface methodology, Construction and Building Materials, 159(517-529) (2018).
[4] J.N. Karadelis, Y. Lin, Flexural strengths and fiber efficiency of steel-fiber-reinforced, roller-compacted, polymer modified concrete, Construction and Building Materials, 93 (2015) 498-505.
[5] Z. Algin, S. Gerginci, Freeze-thaw resistance and water permeability properties of roller compacted concrete produced with macro synthetic fiber, Construction and Building Materials, 234 (2020).
[6] M. Adamu, B.S. Mohammed, M.S. Liew, Mechanical properties and performance of high-volume fly ash roller compacted concrete containing crumb rubber and nano silica, Construction and Building Materials, 171 (2018) 521-538.
[7] A. shafiepour, S. shabani, S. faezi, Effects of Dimensions and Amount of Polymer Fibers on the Strength and Durability of Roller-Compacted Concrete under Freeze-Thaw cycling, Amirkabir Journal of Civil Engineering, 52 (2021) 2593-2606.
[8] C. Hazaree, H. Ceylan, K. Wang, Influences of mixture composition on properties and freeze–thaw resistance of RCC, Construction and Building Materials, 25(1) (2011) 313-319.
[9] G. Chen, M. Yang, L. Xu, Y. Zhang, Y. Wang, Graphene Nanoplatelets Impact on Concrete in Improving Freeze-Thaw Resistance, Applied Sciences, 9(17) (2019) 3582.
[10] L.M. Nicula, O. Corbu, M. Iliescu, Influence of Blast Furnace Slag on the Durability Characteristic of Road Concrete Such as Freeze-Thaw Resistance, Procedia Manufacturing, 46 (2020) 194-201.
[11] Y. Zhang, Y. Wang, M. Yang, H. Wang, G. Chen, S. Zheng, Effect of Graphene Nanoplatelet on the Carbonation Depth of Concrete under Changing Climate Conditions, Applied Sciences, 11(19) (2021) 9265.
[12] D. Harrington, F. Abdo, W.S. Adaska, C. Hazaree, I.S.U.N.C.P.T. Center, P.C. Association, Guide for roller-compacted concrete pavements National Concrete Pavement Technology Center, 2010.
[13] A.C. Institute, Guide for Construction of Concrete Pavements and Bases, in, ACI 325.9R-91, 1999.
[14] A.C. Institute, Roller Compacted Concrete Pavements, in: ACI 325.10R, 1999.
[15] A.S.f.T. Material, Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing, ASTM C666/C666M −15, 2015.
[16] A.S.f.T. Material, Standard Test Method for Scaling Resistance of Concrete Surfaces Exposed to Deicing Chemicals, ASTM C672/672M _ 03, 2003.
[17] A.S.f.T. Material, Standard Practice for Making and Curing Concrete Test Specimens in the Laboratory, ASTM C192/C192M −00, 2000.
[18] A.S.f.T. Material, Standard Practice for Making Roller-Compacted Concrete in Cylinder Molds Using a Vibrating Table, ASTM C1176 _ 92, 1998. | ||
|
آمار تعداد مشاهده مقاله: 132 تعداد دریافت فایل اصل مقاله: 120 |
||