Synthesis of a pure FeAl with a density greater than 95% of theoretical density by optimizing effective factors | ||
| AUT Journal of Mechanical Engineering | ||
| مقاله 10، دوره 5، شماره 2، تابستان 2021، صفحه 329-340 اصل مقاله (1.47 M) | ||
| نوع مقاله: Research Article | ||
| شناسه دیجیتال (DOI): 10.22060/ajme.2021.18021.5881 | ||
| نویسندگان | ||
| Razieh Khoshhal* 1؛ Hojjat Mirzaei-Ghasabe2؛ Ali Hosseinzadeh3 | ||
| 1Department of Material Science and Engineering, Birjand University of Technology, Birjand, Iran | ||
| 2Department of Materials Science and Engineering, Iran University of Science and Technology | ||
| 3Department of Mechanics, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran | ||
| چکیده | ||
| In this study, the FeAl with a density greater than 95% of the theoretical density was synthesized by optimizing the compacting pressure, the particle size of iron and aluminum, and the pre-heating temperature. To do so, the products of the samples which were examined by the change of the particle size of 10µm and 50µm, the pre-heating temperatures of 25°C, 287°C and 550°C and the compacting pressures of 400MPa, 500MPa, and 600MPa, were studied. According to the appearance, composition, density, hardness, and oxidation resistance, the optimum sample was determined. The optimal FeAl had a density of more than 95% of the theoretical density, which was prepared using the particle size of 10/10 of iron and aluminum, the pre-heating temperature of 550°C, and the compacting pressure of 500 MPa. The duration of the pre-heating and the synthesis was also 5 and 3h, respectively. It was found that without pre-heating, there is no possibility of producing a compact and dense product. It was also found that the particle size of the iron is more effective than the particle size of aluminum to achieve the qualified FeAl product. | ||
| کلیدواژهها | ||
| Compacting pressure؛ Particle size؛ Pre-heating temperature؛ FeAl intermetallic؛ Density | ||
| مراجع | ||
|
| ||
|
آمار تعداد مشاهده مقاله: 798 تعداد دریافت فایل اصل مقاله: 520 |
||
| تعداد نشریات | 9 |
| تعداد شمارهها | 455 |
| تعداد مقالات | 5,771 |
| تعداد مشاهده مقاله | 8,376,200 |
| تعداد دریافت فایل اصل مقاله | 6,935,633 |